Implementační normy: Bezešvá ocelová trubka GB/T8162 pro konstrukci, Bezešvá ocelová trubka GB/T8163 pro dopravu tekutin. Mechanické vlastnosti 0420D a 0420E: pevnost v tahu 520~680MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
Způsob výroby trubek: Trubky lze také vyrábět kontinuálním litím, litím do formy nebo válcováním za tepla.
Plynule lité trubky by také měly odpovídat předpisům YB/T 4149; horké trubky by také měly splňovat předpisy YB/T 5221 nebo YB/T 5222; trubky lité do formy mohou také odkazovat na předpisy pro horké (kované) trubky.